NY-P2/NY-P2P
Low Dk 3.50@10GHz，Low Df 0.0025@10GHz）
High Tg Lead-free compatible
Low Z-axis CTE offering superior PTH reliability
Low Water Absorption
-
RF -
Server -
Base Station -
Switch
Typical Properties for NY-P2 Laminate
| 屬性 Property | 項目 Item | 測試方法 IPC-TM-650 | 測試條件 Test Condition | 單位 Unit | 典型值 Typical Value | |
| 熱性能 Thermal | 玻璃態轉換溫度 Tg Glass Transition Temperature | 2.4.25 | DSC | ℃ | \ | |
| 2.4.24 | TMA | ℃ | 190 | |||
| 2.4.24.4 | DMA | ℃ | 230 | |||
| X/Y軸熱膨脹系數（1078×20） X/Y-axis CTE | 2.4.24.5 | ＜Tg,TMA | ppm/°C | 20\21 | ||
| Z軸熱膨脹系數（2116×12） Z-axis CTE | 2.4.24 | ＜Tg,TMA | ppm/°C | 45 | ||
| ＞Tg,TMA | ppm/°C | 270 | ||||
| 2.4.24 | 50~260℃ | % | 2.5 | |||
| 熱分解溫度 Td Decomposition Temperature | 2.4.24.6 | TGA(5%W.L) | ℃ | 400 | ||
| 耐熱性 T288 Thermal Resistance | 2.4.24.1 | Clad | Min | ＞120 | ||
| Etched | Min | ＞120 | ||||
| 電性能 Electrical | 介電常數 Dk (R/C:55%/70%) Permittivity | 1MHz | 2.5.5.9 | C-24/23/50 | — | \ |
| 1GHz | 3.44\3.19 | |||||
| 10GHz | SPDR method | 3.50\3.20 | ||||
| 介質損耗 Df (R/C:55%/70%) Loss Tangent | 1MHz | 2.5.5.9 | C-24/23/50 | — | \ | |
| 1GHz | — | 0.0013\0.0012 | ||||
| 10GHz | SPDR method | 0.0025\0.0020 | ||||
| 體積電阻 Volume Resistivity | 2.5.17.1 | C-96/35/90 | MΩ-cm | 2.4×109 | ||
| 表面電阻 Surface Resistivity | MΩ | 1.9×108 | ||||
| 物理性能 Physical | 吸水率 Water Absorption | 2.6.2.1 | E-1/105+D-24/23 | % | 0.10 | |
| 剝離強度(HTE) Peel Strength | 1oz | 2.4.8 | As Received | N/mm | \ | |
| 剝離強度(RTF) Peel Strength | 1oz | \ | ||||
| 剝離強度(HVLP) Peel Strength | 1oz | 0.7 | ||||
| 彎曲強度 Flexural Strength | Warp | 2.4.4 | As Received | N/mm2 | 475 | |
| Fill | 439 | |||||
| 耐燃性 Flame Resistance | UL-94 | A&E-4/125 | — | V-0 | ||